Structures by: Yakubovich O.
Total: 11
Rubidium nickel-iron borophosphate
B8FeH12Ni5O56P12,0.52(Rb2),2.96(Rb)
Dalton transactions (Cambridge, England : 2003) (2019) 48, 24 8835-8842
a=9.4599(4)Å b=12.2035(4)Å c=19.9085(6)Å
α=90° β=90° γ=90°
Caesium copper borophosphate
B8Cu6H12O56P12,4(Cs)
Dalton transactions (Cambridge, England : 2003) (2019) 48, 24 8835-8842
a=9.4057(5)Å b=12.9274(5)Å c=19.3912(9)Å
α=90° β=90° γ=90°
Caesium nickel borophosphate
B8H12Ni6O56P12,4(Cs)
Dalton transactions (Cambridge, England : 2003) (2019) 48, 24 8835-8842
a=9.5200(4)Å b=12.2546(5)Å c=19.9660(6)Å
α=90° β=90° γ=90°
Sodium zinc aluminium phosphate
AlNaO8P2Zn
Acta Crystallographica Section C (2019) 75, 5 514-522
a=9.5199(3)Å b=8.6700(2)Å c=9.5471(3)Å
α=90° β=119.158(5)° γ=90°
Potassium copper aluminium phosphate
AlCuKO8P2
Acta Crystallographica Section B (2020) 76, 3
a=5.0270(8)Å b=14.047(2)Å c=9.2630(10)Å
α=90° β=102.290(10)° γ=90°
Potassium zinc aluminium phosphate-silicate
Al3K2O16P3SiZn
Acta Crystallographica Section B (2020) 76, 3
a=13.2340(10)Å b=13.1210(10)Å c=8.6581(8)Å
α=90° β=100.140(10)° γ=90°
Caesium borophosphate hydroxide
CsB1P2O6,2(OH)
Acta Crystallographica Section B (2019) 75, 6
a=13.4002(3)Å b=7.4869(2)Å c=14.5329(3)Å
α=90° β=90.059(2)° γ=90°
Caesium manganese borophosphate hydroxide
Cs,Mn,BO8P2,OH
Acta Crystallographica Section B (2019) 75, 6
a=9.1494(3)Å b=8.6991(2)Å c=9.6413(3)Å
α=90° β=100.141(2)° γ=90°
Caesium manganese borophosphate hydrate
Cs0.51Mn1.17,2(H2O),B1P2O8,0.45(H2O)
Acta Crystallographica Section B (2019) 75, 6
a=9.6292(3)Å b=9.6292(3)Å c=15.8051(5)Å
α=90° β=90° γ=120°
Potassium dimanganese trivanadate
KMn2O10V3
Acta Crystallographica Section B (2018) 74, 1 97-103
a=6.912(5)Å b=6.993(5)Å c=9.656(5)Å
α=101.858(5)° β=102.627(5)° γ=100.669(5)°
Dicesium copper tetraaluminate
Cs2CuAl4O8
Acta Crystallographica Section B (2015) 71, 5
a=8.4551(7)Å b=10.0120(10)Å c=17.073(2)Å
α=90° β=101.643(9)° γ=90°